عمود مدور استانلس 310 حراري قطر 8 مم
Stainless Steel 310 Round Bar 8 mm
1.447.00 EGP
For construction parts which should be resistant to scaling up to about 1050°C and extensively inured to the effect of sulfurous gases, especially above 900°C, is very low
اشترك للحصول على أحدث التدوينات المرسلة إلى بريدك الإلكتروني.
| Element | % Present (in product form) | |
|---|---|---|
| C, H, P, L | ||
| Carbon (C) | ≤0.10 | |
| Silicon (Si) | ≤1.50 | |
| Manganese (Mn) | ≤2.00 | |
| Phosphorous (P) | ≤0.045 | |
| Sulfur (S) | ≤0.015 | |
| Chromium (Cr) | 24.00 – 26.00 | |
| Nickel (Ni) | 19.00 – 22.00 | |
| Nitrogen (N) | ≤0.11 | |
| Iron (Fe) | Balance | |
| Product Form | |||||
|---|---|---|---|---|---|
| Thickness a or diamter d (mm) | |||||
| Hardness HB max. 1) 2) 3) | |||||
| Proof Strength3) | |||||
| Rp1.0 N/mm2 | |||||
| Tensile Strength | |||||
| Elongation min. in % | Long Products | ||||
| Flat Products | 0.5 ≤ a/d < 3 | ||||
| 3 ≤ a/d | 354)5) | ||||
| 1% Elongation1) for | ||
|---|---|---|
| Temperature °C | 1,000 h N/mm2 | |
| 600 | 100 | |
| 700 | 45 | |
| 800 | 18 | |
| 900 | 10 | |
| Density at 20°C kg/m3 | 7.9 | |
|---|---|---|
| Thermal Conductivity W/m K at | 20°C | |
| 500°C | 19 | |
| Specific Thermal Capacity at 20°C J/kg K | ||
| Electrical Resistivity at 20°C Ω mm2 /m | ||
| 200°C | 15.5 |
|---|---|
| 400°C | 17.0 |
| 600°C | 17.5 |
| 800°C | 18.5 |
| 1000°C | 19.0 |